Organic dispersion of inorganic nano-platelets

ABSTRACT

Disclosed is an organic dispersion of inorganic platelets, which includes an organic solvent and H-form inorganic platelets dispersed therein. The H-form inorganic platelets have a particle size of between about 20 and 80 nm and the organic dispersion has a sold content of between about 1 and 20 wt %. A method for forming the organic dispersion is also provided.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. application Ser. No. 13/230,671, filed Sep. 12, 2011, which claims priority of Taiwan Patent Application No. 099145159, filed on Dec. 22, 2010, the entirety of which is incorporated by reference herein. The subject matter of this application relates to that of copending application Ser. No. 13/230,701 filed Sep. 12, 2011 for “ORGANIC/INORGANIC COMPOSITE FILM AND METHOD FOR FORMING THE SAME” by Su, Leu and Yang. The disclosure of the copending application is incorporated herein by reference in their entirety.

TECHNICAL FIELD

The present invention relates to an inorganic material, and in particular relates to a dispersion of inorganic nano-platelets.

BACKGROUND

A sol formed from an inorganic material dispersed in an organic solvent has good processability and storability. Silica and metal oxides are typical inorganic materials used for dispersal in an organic solvent. In particular, the silica has advantages such as being cheap, high hardness, a low thermal expansion coefficient or the likes. An organic/inorganic composite material which has both advantages of the inorganic material and the organic material is formed from a mixture of an organic polymer and a sol. Specifically, the organic/inorganic composite material may have a high content of inorganic materials by using a high concentration sol formed from silica type materials.

The different shapes of silica particles, such as a spherical shape, elongated shape or platelet, have different reactivities and are formed from various types of silica aqueous or alcohol dispersion with different processes. Nissan Chemical discloses an elongated shape silica dispersion, for example, referring to U.S. Pat. No. 5,221,497 and U.S. Pat. No. 5,597,212. Also, U.S. Pat. No. 5,902,226 discloses a spherical shape silica. However, the organic dispersion or sol, or even the aqueous dispersion or sol, of the silica platelets, has never been commercially available as spherical or elongated shape silica particles.

Only few references relevantly disclose the silica platelets. For example, U.S. Pat. No. 5,796,177 discloses a method for forming the silica platelets, in which the silica source is mixed with NaOH repeatedly and then thoroughly mixed with Al₂O₃ or ZrO₂ in a high temperature to form the silica platelets. However, the sol of the silica platelets is milk white and opaque. In addition, the silica platelets can only be dispersed in water, and cannot form an organic sol. Moreover, the step of adding NaOH repeatedly reduces process stability.

Silica platelets have a larger surface area than spherical and elongated shape silica particles and its size is also easier to control. Thus, the silica platelets have better applicability. A novel organic dispersion of inorganic platelets is needed to be developed.

SUMMARY

One embodiment of the disclosure provides an organic dispersion of inorganic nano-platelets, including an organic solvent; and H-form inorganic nano-platelets dispersed in the organic solvent, wherein the H-form inorganic nano-platelets have a particle size of between about 20 and 80 nm, and wherein the organic dispersion has a solid content of between about 1 and 20 wt %.

One embodiment of the disclosure provides a method for forming an organic dispersion of inorganic nano-platelets, including: (a) dispersing inorganic nano-platelets into water to form an aqueous dispersion; (b) performing an ion-exchange procedure to the inorganic nano-platelets by adding an ion-exchange resin thereto, for forming an aqueous dispersion of an H-form inorganic nano-platelets; (c) adding the aqueous dispersion of an H-form inorganic nano-platelets into a mixture of a first organic solvent and a second organic solvent; and (d) removing the first solvent and water for dispersing the H-form inorganic nano-platelets into the second organic solvent.

A detailed description is given in the following embodiments with reference to the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The disclosure can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:

FIG. 1 shows the XRD spectrums of the non-processed inorganic platelets and the H-form inorganic platelets in Example 1.

FIG. 2 shows the TEM image of the H-form inorganic platelets in Example 1.

DETAILED DESCRIPTION

The following description is of the best-contemplated mode of carrying out the invention. This description is made for the purpose of illustrating the general principles of the invention and should not be taken in a limiting sense. These are, of course, merely examples and are not intended to be limiting. The scope of the invention is best determined by reference to the appended claims.

In conventional method for forming an organic dispersion of inorganic materials, clay is dispersed in water, and then metal cations of the clay are exchanged with quaternary ammoniums such that the clay is transformed to organic clay for dispersing in an organic solvent. Alternatively, a water soluble polymer is added to the clay aqueous dispersion to open the layered structure of the clay, which is referred to as intercalation. In the first method, the resulting composite material does not have much inorganic content. In the second method, the resulting composite material has a low crack temperature and poor water resistance due to the hydrophilic property of the water soluble polymer.

The present invention provides an organic dispersion of inorganic nano-platelets and a method for forming the same, in which the metal ions of the inorganic nano-platelets are directly exchanged with hydrogen ions by an ion-exchange procedure and no dispersing agents or modifying agents are added. Thus, compared to the conventional method which uses the quaternary ammonium salt or the water soluble polymer to perform intercalation, only a simple process is needed. Furthermore, the inorganic nano-platelets may maintain their shape and size after transfer to the organic solvent. The resulting organic dispersion of inorganic nano-platelets may have a high solid content.

According to the embodiments of forming an organic dispersion of inorganic nano-platelets, an aqueous dispersion of inorganic nano-platelets is provided first. The inorganic nano-platelets may be natural or synthetic nano-clay. The nano-clay may have a particle size of between about 1 and 100 nm. It should be noted the transparency of the dispersion should be determined by the size of the clay. For example, the dispersion may be opaque when the clay has a particle size of larger than 100 nm. In one embodiment, the inorganic nano-platelets may have an aspect ratio of not less than 10, preferably between about 20 and 100. The inorganic nano-platelets may include smectite clay, vermiculite, halloysite, sericite, mica, synthetic mica, layered double hydroxide, synthetic smectite clay or combinations thereof. The smectite clay may include montmorillonite, saponite, beidellite, nontronite, hecorite, stevensite or combinations thereof. In one embodiment, the aqueous dispersion may have a solid content of between about 1% and 20%.

Next, an H-form cation ion-exchange resin and an OH-form anion ion-exchange resin are added to the aqueous dispersion to perform an ion-exchange procedure. In this ion-exchange procedure, the metal cations of the inorganic nano-platelets may be replaced with hydrogen ions. In one embodiment, a mole ratio of the H-form cation ion-exchange resin and the OH-form anion ion-exchange resin is about 1:1. As such, the amount of hydrogen ions released from the reaction of the anion ion-exchange resin and the amount of hydroxide ions released from the reaction of the cation ion-exchange resin can be maintained substantially equal. In one embodiment, the H-form ion-exchange resin may be DOWEX® H-form resins, and the OH-form anion ion-exchange resin may be DOWEX® OH-form resins.

After the ion-exchange procedure, all of the inorganic nano-platelets are transformed to the H-form inorganic nano-platelets. Accordingly, the layered structure of the inorganic nano-platelets may be opened resulting in the H-form inorganic nano-platelets to be uniformly dispersed in the water by means of a smaller particle size.

Next, the aqueous dispersion of the H-form inorganic nano-platelets is thoroughly mixed with a mixture of a first organic solvent and a second organic solvent for transferring the H-form inorganic nano-platelets to the phase of the first and the second organic solvent. The first organic solvent may include any organic solvents soluble with the second organic solvent and water. For example, the first organic solvent may include any alcohol soluble with water, ethyl ether, acetone or combinations thereof. In a preferred embodiment, the first organic solvent may be isopropanol. A ratio of the water and the first organic solvent is about between 1:1 and 1:3, and a ratio of the water and the second organic solvent is between about 1:0.07 and 1:3. The second organic solvent may include N-methyl-2-pyrrolidone (NMP), N,N-dimethyl acetamide (DMAc), γ-butyrolactone (GBL), N,N-dimethylformamide (DMF), dimethyl sulfoxide (DMSO), xylene, toluene or combinations thereof. Note that the boiling points of the water and the first organic solvent may be preferably lower than that of the second organic solvent such that the water and first organic solvent can be removed simultaneously in sequential processes. The amount of the second organic solvent may contribute to the solid content of the resulted organic dispersion; however, one skilled in the art should understand that the ratio of the first organic solvent and the second solvent can be variously changed according to the types of the first organic solvent and the second organic solvent.

Next, the water and the first organic solvent are removed by a vacuum decompression concentration such that the H-form inorganic nano-platelets are all dispersed in the second organic solvent for forming the organic dispersion of the H-form inorganic nano-platelets. In the present embodiment, the organic dispersion of the H-form inorganic platelets may have a solid content of between about 1 and 20 wt %, a plate shape, a particle size of between about 20 and 80 nm and an aspect ratio of not less than 10 or preferably between about 20 and 100. The organic dispersion may have a transparency larger than 90%.

To summarize, the present invention provides a dispersion of inorganic platelets, and in particular, the dispersion may be an organic dispersion. Compared to the conventional method which uses quandary ammonium salts and hydrophilic polymer, only simple processes such as ion-exchange and phase transfer procedures are needed to be performed. Furthermore, it is unnecessary to use any salts, polymers or other additives. Thus, the resulting inorganic platelets may have better applicability. For example, the advantages such as high thermal resistance and ultra low thermal expansion coefficient of the inorganic platelets are not influenced by the addition of the additives. Thus, the organic dispersion of inorganic platelets may have good storage stability. Meanwhile, when forming an organic/inorganic composite material with an organic polymer, the inorganic nano-platelets can be uniformly dispersed because their size is still maintained in nano-scale and the organic dispersion is highly soluble with the organic polymer.

Below, exemplary embodiments will be described in detail with reference to accompanying drawings so as to be easily realized by a person having ordinary knowledge in the art. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.

EXAMPLES Comparative Example 1

800 g of a clay platelets aqueous dispersion having a solid content of 20.2 wt % and a pH value of 2.8 was prepared. Next, the clay platelets aqueous dispersion was mixed with various ratios of water, AlCl₃ aqueous solution and NaOH solution, repeatedly. Finally, a clay platelets aqueous dispersion having a pH value of 7.64 was obtained. The clay platelets had a particle size of 370 nm. The aqueous dispersion had a solid content of 15 wt %, which was milky white when observed (detailed procedures are disclosed in U.S. Pat. No. 5,196,177).

Example 1

30 g of clay platelets (Laponite RDS, particle size of 20 nm×20 nm×1 nm) was dispersed in 970 g of deionic water to form 1000 g of 3 wt % of a clay platelets aqueous dispersion. Next, 300 g of an H-form cation ion-exchange resin (Dowex H form) and 300 g of OH from anion ion-exchange resin (Dowex OH form) were added to the clay platelets aqueous dispersion to perform ion-exchange. After filtering, 960 g of 1.8 wt % of an H-form clay platelets aqueous dispersion was obtained. Then, the H-form clay platelets aqueous dispersion was thoroughly mixed with 1440 g of isopropanol and 328.3 g of DMAc. Isopropanol and DMAc were removed by vacuum decompression concentration and 338.8 g of an H-form clay organic dispersion was obtained. The H-form clay platelets organic dispersion had a solid content of 5.1 wt %, and was transparent when observed. The structure of the H-form clay platelets were characterized by XRD, as shown in FIG. 1. The particle size of the H-form clay platelets was 20 nm×20 nm×1 nm, characterized by a TEM image, as shown in FIG. 2.

Example 2

The same procedures as in Example 1 were repeated except that 270. 2 g of DMAc was added. 278.6 g of an H-form clay organic dispersion (DMAc dispersion) was obtained. The H-form clay organic dispersion had a solid content of 6.2 wt %, and was transparent when observed. The structure of the H-form clay platelets were characterized by XRD. The particle size of the H-form clay platelets was 20 nm×20 nm×1 nm, characterized by a TEM image.

Example 3

60 g of platelets clay (Laponite RDS, particle size of 20 nm×20 nm×1 nm) was dispersed in 970 g of deionic water to form 1000 g of 3 wt % of a clay aqueous dispersion. Next, 300 g of an H-form cation ion-exchange resin (Dowex H form) and 300 g of OH from an anion ion-exchange resin (Dowex OH form) were added to the clay aqueous dispersion to perform ion-exchange. After filtering, 1920 g of 1.7 wt % of an H-form clay aqueous dispersion was obtained. Then, the H-form clay aqueous dispersion was thoroughly mixed with 3800 g of isopropanol and 293.7 g of DMAc. Isopropanol and DMAc were removed by decompression concentration and 315.6 g of an H-form clay organic dispersion was obtained. The structure of the H-form clay platelets were characterized by XRD. The particle size of the H-form clay platelets was 20 nm×20 nm×1 nm, characterized by a TEM image.

Example 4

The same procedures as in Example 3 were repeated except that the 260.2 g of DMAc was added. 248.3 g of an H-form clay organic dispersion (DMAc dispersion) was obtained. The H-form clay organic dispersion had a solid content of 13.1 wt %, and was transparent when observed. The structure of the H-form clay platelets were characterized by XRD. The particle size of the H-form clay platelets was 20 nm×20 nm×1 nm, characterized by a TEM image.

Example 5

The H-form clay organic dispersions in Examples 1-4 were placed in an ambient environment for longer than one month. The particle sizes of the H-form clay platelets were still maintained and the dispersions were still transparent. The results are summarized in Table 1.

TABLE 1 Example 1 2 3 4 Storage longer than one longer than one longer than one longer than time month month month one month

FIG. 1 shows the XRD (X-ray diffraction) spectrums of the non-processed inorganic platelets and the H-form inorganic platelets in Example 1. As shown in FIG. 1, it is observed that all of the diffraction peaks of the H-form inorganic platelets in Example 1 (solid line) were the same with the non-processed inorganic platelets (dotted line). It can be suggested that the H-form inorganic platelets still had the plate shaped crystalline. FIG. 2 shows the TEM (transmission electron microscopy) image of the H-form inorganic platelets in Example 1. As shown in FIG. 2, plate shaped particles with a particle size of between about 20 and 80 nm was observed, which are significantly smaller than that (370 nm) of the inorganic platelets in Comparative Example 1.

It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed methods and materials. It is intended that the specification and examples be considered as exemplary only, with a true scope of the disclosure being indicated by the following claims and their equivalents. 

What is claimed is:
 1. An organic dispersion of inorganic nano-platelets, comprising an organic solvent; and H-form inorganic nano-platelets dispersed in the organic solvent, wherein the H-form inorganic nano-platelets have a particle size of between about 20 and 80 nm, and wherein the organic dispersion has a solid content of between about 1 and 20 wt%, wherein the H-form inorganic nano-platelets include protons directly connected to inorganic nano-platelets.
 2. The organic dispersion of inorganic nano-platelets as claimed in claim 1, wherein the H-form inorganic nano-platelets comprises an H-form type of smectite clay, vermiculite, halloysite, sericite, mica, synthetic mica, layered double hydroxide, smectite clay or combinations thereof.
 3. The organic dispersion of inorganic nano-platelets as claimed in claim 2, wherein the smectite clay comprises montmorillonite, saponite, beidellite, nontronite, hecorite, stevensite or combinations thereof.
 4. The organic dispersion of inorganic nano-platelets as claimed in claim 1, wherein the organic solvent comprises N-methyl-2-pyrrolidone (NMP), N,N-dimethyl acetamide (DMAc), γ-butyrolactone (GBL), N,N-dimethylformamide (DMF), dimethyl sulfoxide (DMSO), xylene, toluene or combinations thereof.
 5. The organic dispersion of inorganic nano-platelets as claimed in claim 1, wherein the H-form inorganic nano-platelets have an aspect ratio greater than
 10. 6. The organic dispersion of inorganic nano-platelets as claimed in claim 1, wherein the organic dispersion has a transparency larger than 90%. 